Synthesis and properties of isosorbitol-type polycarbonate copolymers with high molecular weight
Materials & Applications | 更新时间：2025-11-14

    • Synthesis and properties of isosorbitol-type polycarbonate copolymers with high molecular weight

    • “In the field of materials science, researchers have successfully prepared isosorbide based polycarbonate materials with high molecular weight, high strength, good flexibility, and high transparency by introducing bio based raw materials.”
    • Engineering Plastics Application   Vol. 53, Issue 10, Pages: 39-47(2025)

    • DOI：10.3969/j.issn.1001-3539.2025.10.006    

      CLC： TQ324.8

    • Received：29 July 2025，

      Revised：2025-09-12，

      Accepted：12 September 2025，

      Published：10 October 2025

    移动端阅览

  • YANG Chao，LIU Hongyu，ZHONG Jiachun，et al. Synthesis and properties of isosorbitol-type polycarbonate copolymers with high molecular weight[J]. Engineering Plastics Application，2025，53(10)：39-47. DOI： 10.3969/j.issn.1001-3539.2025.10.006.

  •  
  •  

0

Views

9

下载量

0

CSCD

Alert me when the article has been cited
提交
Tools
Download
Export Citation
Share
Add to favorites
Add to my album

Related Articles

Temperature correlation of mechanical properties strengthening of polycarbonate after extrusion deformation
Synthesis of high molecular weight polylactic acid by melt polymerization and its toughening modification
Preparation of PETG/PC/PBAT composite fibers based on melt spinning method
Research progress on synthesis of isosorbide and its plasticization effect
Preparation of high impact PC/ABS alloy and resin selection

Related Author

WANG Bolun
WANG Tao
GE Yong
SUN Qiwei
LANG Jianlin
YAN Yue
HU Mingguang
BAI Lu

Related Institution

Baimtec Material Co.，Ltd.
Beijing Engineering Research Center of Advanced Structural Transparence for;the Modern Traffic System
School of Material Science and Engineering，East China University of Science and;Technology
Institute of Energy Resources，Hebei Academy of Sciences
Julu County Applied Technology Research Institute
0