《工程塑料应用》 2021年第01期
DOI:10.3969/j.issn.1001-3539.2021.01.012
基于田口试验法的熔融沉积成型PLA制品工艺优化
文周12,薛美贵1,王旭红1
1.东莞职业技术学院,广东东莞 523808; 2.西安科技大学机械学院,西安 710054 
Optimization of PLA Product Process by Melt Deposition Based on Taguchi Test
Wen Zhou12, Xue Meigui1, Wang Xuhong1
1. Dongguan Polytechnic, Dongguan 523808, China; 2. College of Mechanical Engineering, Xi'an University of Science and Technology, Xi'an 710054, China 
摘要:为了提高熔融沉积成型(FDM)制品的质量,采用田口试验法研究填充密度、沉积方向和填充图案三个因素对聚乳酸(PLA)制品拉伸性能的影响。结果表明,加工工艺参数对拉伸弹性模量和拉伸强度的影响程度均为沉积方向>填充密度>填充图案,其中拉伸弹性模量最优化的参数组合为填充密度100%、沉积方向45°、填充图案网格形状,拉伸强度最优化的参数组合为填充密度70%、沉积方向45°、填充图案网格形状。通过扫描电子显微镜对拉伸试验失效断面进行观察分析,探究了FDM打印工艺参数之沉积方向、填充密度对PLA试样拉伸失效的影响及其失效机理,其表征分析与试验结果高度吻合,表明该研究结果具有较好的借鉴意义。 
Abstract:In order to improve the quality of fused deposition modeling (FDM) printed products, taguchi test was used to study the effects of filling density, deposition direction and filling pattern on the tensile properties of PLA products. The results show that the influence of processing parameters on the elastic modulus and tensile strength is as follows: deposition direction > filling density > filling pattern; the optimal parameter combination for elastic modulus is the filling density of 100%, the deposition direction of 45° and the filling pattern mesh shape; the optimal parameter combination for tensile strength is 70% of the filling density, 45° in the deposition direction and the mesh shape of the filling pattern. The failure section of tensile test was observed and analyzed by scanning electron microscopy, and the influence of the deposition direction and filling density of FDM printing process parameters on the tensile failure of PLA samples and the failure mechanism were investigated. The characterization and analysis are highly consistent with the test results, indicating that the research results are of good reference significance. 
关键词:熔融沉积成型;打印参数;田口试验;拉伸性能 
Keywords:fused deposition modeling; printing parameter; taguchi method; tensile behavior 
基金:国家自然科学基金(11972282)、陕西省自然科学基金(2018 JZ1001)、东莞市科技特派员项目 
本文引用格式:
文周,薛美贵,王旭红.基于田口试验法的熔融沉积成型PLA制品工艺优化[J].工程塑料应用,2021,49(1):58-62.
Wen Zhou,Xue Meigui,Wang Xuhong. Optimization of PLA product process by melt deposition based on taguchi test[J]. Engineering Plastics Application,2021,49(1):58-62. 

原文:
 
相似文章:
  熔融沉积成型聚醚醚酮热处理工艺对力学性能影响
2021年第02期
  熔融沉积成型打印ABS挤出胀大现象
2020年第10期
  2,4-二甲基咪唑封闭聚氨酯制备及性能
2020年第09期
  PA6/石墨烯复合材料制备及拉伸性能
2020年第07期
  不同固体润滑填料对聚四氟乙烯性能的影响
2020年第06期
  PLA增强改性PBS共混物制备及性能
2020年第05期
  紫外吸收剂DPP对PE-LD棚膜性能的影响
2020年第02期
  聚酰亚胺填充聚四氟乙烯密封材料的性能
2019年第11期
  工艺参数对SLA成型制件力学性能的影响
2019年第10期
  打印参数对FDM成型ABS制品性能的影响
2019年第10期
《工程塑料应用》杂志社 版权所有,未经授权禁止复制或者建立镜像
地址:山东省济南市天桥区田庄东路3号 邮编:250031
电话:0531-85878057 85878223 85878148 85878278
鲁ICP备05018524号-5