《工程塑料应用》 2021年第01期
DOI:10.3969/j.issn.1001-3539.2021.01.007
PMMA/棉花纤维素复合薄膜的制备及性能
孙浩炯,尚蒙娅,贾冬晴,孙铭,安蒙恩,唐哲
河南工业大学材料科学与工程学院,郑州 450001 
Preparation and Properties of PMMA/Cotton Cellulose Composite Films
Sun Haojiong, Shang Mengya, Jia Dongqing, Sun Ming, An Mengen, Tang Zhe
School of Material Science & Engineering, Henan University of Technology, Zhengzhou 450001, China 
摘要:为改善聚甲基丙烯酸甲酯(PMMA)的热性能和力学性能,以经过预处理的棉花纤维素为增强体,将PMMA与棉花纤维素溶液按不同比例混合,利用溶液浇铸法制备PMMA/棉花纤维素复合薄膜,并利用热重分析、透光性分析以及拉伸性能测试研究了不同棉花纤维素含量的PMMA/棉花纤维素复合薄膜的性能。结果表明,与PMMA薄膜相比,PMMA/纤维素复合薄膜的热稳定性和力学性能均有所提升,PMMA/纤维素复合薄膜的热分解温度提高8.3%;随着棉花纤维素含量从0增加到15%,拉伸强度从10.53 MPa提升到55.95 MPa,最高提升了431%。此外,复合薄膜的光透过率随着棉花纤维素含量的增加而降低。当棉花纤维素含量为7.5%时,复合薄膜不仅具有良好的力学性能,而且具有较高的透光率,综合性能较好。 
Abstract:In order to improve the thermal and mechanical properties of polymethyl methacrylate (PMMA), PMMA/cotton cellulose composite films were prepared by solution casting method with PMMA as substrate and pretreated cotton cellulose as reinforcement. The properties of PMMA/cotton cellulose composite films with different contents of cotton cellulose were studied by thermogravimetric analysis, transmittance analysis and tensile test. The results show that compared with pure PMMA film, the thermal stability and mechanical properties of PMMA/cellulose composite film are improved. The thermal decomposition temperature of PMMA/cellulose composite film increases by 8.3%. With the content of cotton cellulose increasing from 0 to 15%, the tensile strength increases from 10.53 MPa to 55.95 MPa, and the strength increases by 431% when the content is 15%. In addition, the light transmittance of the composite film decreases with the increasement of the content of cotton cellulose. When the content of the cotton cellulose is 7.5%, the composite film not only has good mechanical properties, but also has high transmittance, which shows a good comprehensive performance. 
关键词:聚甲基丙烯酸甲酯;棉花纤维素;复合薄膜;热性能;力学性能 
Keywords:polymethyl methacrylate; cotton cellulose; composite film; thermal property; mechanical property 
基金:河南工业大学高层次人才科研启动基金项目(2019BS010),河南工业大学创新基金支持计划专项项目(2020ZKCJ07) 
本文引用格式:
孙浩炯,尚蒙娅,贾冬晴,等. PMMA/棉花纤维素复合薄膜的制备及性能[J].工程塑料应用,2021,49(1):34-39.
Sun Haojiong,Shang Mengya,Jia Dongqing,et al. Preparation and properties of PMMA/cotton cellulose composite films[J]. Engineering Plastics Application,2021,49(1):34-39. 

原文:
 
相似文章:
  热塑性聚氨酯基导热纳米复合材料的制备及性能研究进展
2021年第03期
  多面体低聚倍半硅氧烷对环氧树脂热性能影响分析
2021年第03期
  油茶果壳对PE-HD力学性能的影响
2021年第03期
  长玻纤增强聚丙烯复合材料的制备及力学性能
2021年第03期
  P(VDF-HFP)/BST纳米复合薄膜的制备及介电、储能性能
2021年第03期
  石墨烯/二氧化钛对PVC薄膜性能影响
2021年第02期
  不同促进剂对PP/PP-g-MAH/脱硫胶粉共混物性能影响
2021年第02期
  热处理温度对对位芳纶纤维表面聚集态结构和性能影响
2021年第02期
  熔融沉积成型聚醚醚酮热处理工艺对力学性能影响
2021年第02期
  环氧树脂/石英纤维透波复合材料制备
2021年第02期
《工程塑料应用》杂志社 版权所有,未经授权禁止复制或者建立镜像
地址:山东省济南市天桥区田庄东路3号 邮编:250031
电话:0531-85878057 85878223 85878148 85878278
鲁ICP备05018524号-5